FKM RAW RUBBER(PEROXIDE CURING) - FP600GF

 

► FP600GF(FKM RAW RUBBER-PEROXIDE CURING) is a peroxide-cured terpolymer fluororubber composed of vinylidene fluoride, hexafluoropropylene, etrafluoroethylene and vulcanization point monomers.

 

 

► Basic parameters

 

PROPERTY	TEST VALUE
Mooney viscosity, ML (1+10') at 121 ℃	60 ± 5
Fluorine content	70
Specific gravity	1.86
Appearance	Translucent
Soluble solvents	Esters, Ketones

 

► Typical vulcanization properties

 

FORMULA	PHR
FP600GF	100
ZnO	3
HT-290	0.5
N990 MT Carbon Black	30
TAIC70	4
Luperox 101XL45	2.5
MDR 6 min @ 175 ℃ arc 0.5
MH	18
ML	1.3
TS2	38
TC50	60
TC90	153

 

► Typical mechnical properties

 

Press cure: 10 min @ 170 ℃, Post cure: 4H @ 232 ℃
Hardness, shore A	76
100% modulus, MPa	6.21
Tensile strength, MPa	19.2
Eongation at break, %	220
ASTM D395, DIE B, 200 ℃ * 70 H * 25 %
Compression set	23
Low temperature resistance
TR10(ASTM D1329), ℃	-8
Methanol resistance 23 ℃ * 70 H
Δ Volume, %	3.5

 

 

Mixing:  FP600GF(FKM RAW RUBBER-PEROXIDE CURING) can be mixed in a standard water-cooled internal mixer or a two-roll open mixer. The fillers and compounding agents used in the formula are the same as those in ordinary fluororubber. All compounding agents must be mixed before adding to the rubber. Adequate cooling must be ensured during the mixing process. After mixing, the rubber should be cooled as soon as possible.

 

 

FP600GF (FKM RAW RUBBER-PEROXIDE CURING)is packed in cartons lined with PE film, with a net weight of 25kg per carton.

 

 

Try to avoid contact with skin and eyes, and avoid inhaling combustion gases. Smoking is prohibited in the workplace. Wash with clean water before eating or smoking. For more health and safety information, please refer to the MSDS.

 

 

 

 

 

Hot Tags: fkm raw rubber(peroxide curing) - fp600gf, China fkm raw rubber(peroxide curing) - fp600gf manufacturers, suppliers, factory, FFKM O ring, FDA Grade FKM, rubber sheet, Oil Resistance Silicone, FKM Hose, NBR Compound